Low loss visible-IR transmitting glass-aluminum oxynitride composites and process

ABSTRACT

This invention pertains to a composite of AlON and a germanate glass, and to a process for bonding AlON to the glass. The composite includes AlON and glass bonded together and having transmission in the visible and mid-infrared wavelength region. The process includes the step of heating them together above the softening temperature of the glass, the composite having excellent, i.e., typically in excess of about 60%, transmission in the 0.4-5 wavelength region.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention pertains to composites of germanate glass, particularlyto barium gallogermanate (BGG) glass and aluminum oxynitride (AlON), andto a process for forming the composites by bonding the glass and theAlON.

2. Description of Related Art

Several sensors, operating in vis-IR region of 0.4-5.0 μm wavelength,currently use polycrystalline ZnS , which includes multi-spectral ZnSand CLEARTRAN®, hereinafter referred as zinc sulfide (ZnS), as a windowmaterial. ZnS is a very soft material, easily scratched and thereforenot useful in rugged environments. It also has limited transmission inthe visible wavelength region. Recently, new window materials have beendeveloped, including BGG glass, Spinel and AlON, which are 3-10 timesharder and 2-10 times stronger than ZnS.

Transparent AlON is a polycrystalline ceramic material, which is made bya cold isostatic pressing process followed by sintering and a hotisostatic pressing process. Large AlON windows are currently beingdeveloped for potential military applications, including sensor windowsand domes on aircraft, reconnaissance windows on aircraft and unmannedairborne vehicles, missile domes and windshields for vehicles. AlON canalso find many commercial applications, such as armor windows onbuildings, banks, aircrafts, cars, etc.

AlON is a very hard material and, consequently, its grinding andpolishing costs are high. Applying a glass coating on the AlON substratecan significantly reduce its grinding and polishing costs. The indexrefraction of the glass and AlON can be matched to minimize reflectionlosses. The glass can be readily polished using traditional glasspolishing techniques and therefore considerably reduce the polishingcosts of AlON.

A new product is disclosed herein based on a germanate glass-AlONcomposite article. The new germanate glass is designed so that it can beeasily bonded to an AlON substrate. The process for bonding the newglass to an AlON substrate is also disclosed. The bonded composite isvery strong and withstands chemical and environmental abuse. The glassacts as an excellent dielectric layer in missile domes and windowdesigns for applications requiring transmission in the visible, IR andmicrowave frequencies. For example, the composite can contain anelectromagnetic interference (EMI) grid.

Many of the barium gallogermanate (BGG) glasses disclosed in the U.S.Pat. No. 5,305,414 cannot be used here because of the large coefficientof thermal expansion mismatch with AlON. Due to this large coefficientof thermal expansion mismatch, the prior art BGG glass delaminates fromAlON substrates during thermal cycling. The BGG glass suitable hereinbonds very well to AlON and does not delaminate.

OBJECTS AND SUMMARY OF THE INVENTION

An object of this invention is a composite of a barium gallogermanateglass, or any other suitable germanate glass, properly bonded to AlON.

Another object of this invention is a composite of a BGG glass and AlONthat has excellent transmission in the wavelength range of 0.4-5 μm.

Another object of this invention is a composite of a BGG glass and AlONthat has matched coefficient of thermal expansion and index ofrefraction of the glass and the AlON.

Another object of this invention is the procedure for bonding a softerBGG glass substrate and a harder AlON substrate to realize cost savingin polishing the composite.

Another object of this invention pertains to a process for bonding a BGGglass to AlON.

Another object of this invention pertains to the use of alumina topromote adhesion between BGG glass and AlON during fabrication of theresulting composite.

These and other objects of this invention can be achieved by bonding aBGG glass and AlON to form a composite thereof that can be polished onthe glass side and thus save the polishing cost since the BGG glass issofter than AlON.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic diagram of a composite of an AlON substrate and aBGG glass substrate in the shape of a dome.

FIG. 2 is a differential thermal analysis trace of the BGG glass 15BaO/10 Ga₂O₃/5 Al₂O₃/70 GaO₂ showing glass transmission temperature(T_(g)) of 659° C., crystallization temperature (T_(x)) of 817° C. andglass stability temperature (T_(x)−T_(g)), or working range, of about158° C.

FIG. 3 is a picture showing excellent transmission of the BGG glass andthe AlON composite window, as discussed in Example 3.

FIG. 4 shows BGG glass-AlON composite joined by the glass between theAlON substrates.

DETAILED DESCRIPTION OF THE INVENTION

This invention, in a preferred embodiment, is directed to a new BGGglass-AlON composite and to a process for making it which requiresmatched coefficient of thermal expansion, matched refractive index ofAlON and BGG glass, wetting, and bonding. The glass does not have to belimited to BGG glass and may include other germanate glasses. By theterm “germanate glass” it is meant that GeO₂ is the major glass former.The composite has excellent transmission in the 0.4-5 μm wavelengthregion that is suitable for various military and commercial visible andmid IR applications in lenses, optical devices, windows, domes and othergeometric structures such as IRCM jam heads, visible IR windows, and thelike. The BGG glass is designed with a coefficient of thermal expansionwithin 1×10⁻⁶ /K, and typically within 0.1×10⁻⁶/K of the value for AlONand refractive index of the glass is within 0.1, and typically within0.05 of AlON. Depending on application, thickness of AlON is typically1-5, and more typically about 2 millimeters. The bond between the glassand the AlON is very stable and survives repeated thermal cyclingwithout delaminating.

AlON has a defect cubic spinel crystal structure with chemical formulaof Al_((64+x)/3) O_(32−x) N_(x) , where x is 2-5. Nitrogen stabilizesthe cubic spinel crystal structure over a wide composition range. Withthe optical and mechanical properties equivalent to single crystalsapphire, but fabricated using standard low-cost powder-processingtechniques, AlON is showing a lot of promise as a high performanceoptical ceramic. The principle application of the AlON material is inmissile domes and windows and bullet-proof transparent armor.

One of the presently used processes to make AlON begins with synthesisof optical quality AlON powder, followed by the formation of a greenbody using conventional forming techniques. A heat treatment process isthen used to achieve 100 % density. The fully dense ceramic is then cut,ground and polished into a finished product at a significantly lowercost than sapphire.

Some of the physical parameters of AlON and the BGG glass of compositionof 15 BaO-10 Ga₂O₃-5 Al₂ O₃-70 GeO₂, are given in Table I, below: TABLEI AlON BGG Glass* Density, g/cc 3.69 4.5 Hardness, kg/mm² 1970 450Flexure Strength, MPa 300 100 Fracture Toughness 1.4 0.7 RefractiveIndex 1.67 1.7 Change in RI with Temperature 13 8 Coefficient of ThermalExpansion, (×10⁻⁶/K) 5.8 5.9 Thermal Conductivity, W/mK 11 1Transmission Window, μm 0.3-5.0 0.4-5.0

The BGG glass of this invention, which can transmit light over visibleand infrared regions of the light spectra, is characterized by acomposition that contains three principal components, although, itshould be understood that the glass composition described herein cancontain more components than specified herein. The glass compositiondescribed herein contains germanium oxide (GeO₂); barium oxide (BaO);and gallium oxide (Ga₂O₃), or more correctly, gallium sesquioxide. Itshould be understood that other components, such as lanthanum oxide(La₂O₃), aluminum oxide (Al₂O₃) and indium oxide (In₂O₃), and othercomponents such as ZnO, SrO, CaO, ZrO₂, Y₂O₃, Gd₂O₃, Na₂O, K₂O, Rb₂O,Cs₂O, and the like can be included in the glass composition disclosedherein as long as they do not change the character of the glass.

To avoid crystallization, the mole ratio of barium oxide to galliumoxide should be about 2:1 to 1:1, preferably 1.5:1 to 1:1, and amount ofgermanium oxide should be about 50 to 95 mole percent, preferably 65 to90 mole percent, based on the amount of germanium oxide, barium oxideand gallium oxide in the glass composition. If the glass composition ismelted with no intention of processing into a fiber application, amountof germanium oxide in the glass composition can be as low as about 40mole percent and the ratio of barium oxide to gallium oxide can be ashigh as about 4:1 and as low as about 1: 1, on molar basis, in order toavoid crystallization in the glass, where crystallization isundesirable. About 0.1 to about 5 molar percent, preferable 0.5 to 4,gallium oxide in the glass composition can be replaced with a modifyingagent selected from lanthanum oxide or indium oxide or aluminum oxide.This means that if there is 15 mole percent of gallium oxide in a glasscomposition, up to about 5 mole percent of it can be replaced with amodifying agent. Preferred modifying agent is aluminum oxide.

The preferred BGG glass composition is within the glass forming portionof the phase diagram and has the composition of, based on mole percent,3-10 Al₂O₃/10-20 BaO/5-15 Ga₂O₃/60-80 GeO₂, which is purified to containless than 5 ppm OH— ions, and more preferably less than 1 ppm OH— ions.The alumina in the glass composition promotes adhesion between the BGGglass and AlON.

Presence of the modifying agent in the glass composition, describedherein, imparts the advantage of increasing crystallization temperature.For instance, without any modifying agent, crystallization temperatureof a BGG glass composition was 850° C. In the same composition with 2mole percent gallium oxide replaced with lanthanum oxide, i.e., thepreferred modifying agent, crystallization temperature was 903° C.

Glass transition temperatures of the glass compositions described hereinvary from about 600° C. to about 700° C. For instance, at the molarratio of barium oxide to gallium oxide of 1, T_(g) of the glasscomposition containing 40 mole percent germanium oxide is slightly below700° C. Also, at the molar ratio of barium oxide to gallium oxide of 1,the glass composition containing 65 mole percent germanium oxide hasT_(g) of about 667° C. The two glass compositions consisted of onlybarium oxide, gallium oxide and germanium oxide.

The way the glass is formed is by mixing high purity (99.999% plus)barium carbonate, gallium oxide and germanium oxide in a suitable amountfor 2-4 hours; melting the batch thoroughly; and quenching it into aglass cullet. The cullet is then placed in a large platinum crucible,heated to a melting temperature, as described in Example 1, herein. Theglass is then formed into the desired shape. The shaped glass isannealed to relieve any stresses.

Preparation of an AlON-BGG glass composite typically involves cuttingthe BGG glass to the desired AlON substrate size and shape. The glass tobe bonded is then optionally polished, using, for example, 800 grit sizeabrasive paper, and cleaned, typically using isopropyl alcohol.Formation of the bonded composite is typically made in a vacuum or airatmosphere at temperature above T_(g) but below T_(x). A load can beused on the samples during the bonding process.

The glass is bonded to AlON substrate by heating them together above thesoftening temperature of the glass. At this bonding temperature, theglass softens and makes a good pore-free bond with essentially noentrapped air. The bonding procedure also works for AlON withelectromagnetic interference (EMI) grids. The EMI grids are typicallyapplied to windows requiring transmission in the visible-IR region withselective transmission/reflection of certain microwave frequencies. Aslight vacuum can be used at times to assist in making a pore/bubblefree joint between the two substrates. Once the glass is joined to theAlON substrate above the softening temperature of the glass, the glassis slowly cooled to the annealing temperature to release any thermalstresses followed by slow cooling to room temperature.

More specifically, depending on application, either the glass or theAlON substrates, or both, can be pre-treated before forming thecomposite. For instance, an electromagnetic interference grid can beapplied to the AlON before forming the composite.

The resulting composite has an excellent joint that does not separate onrepeated cycling and can easily be polished and handled withoutdelamination. In preparing a particular type of a preferred embodimentof the invention, containing an EMI grid, for a missile dome, forexample, the following steps are employed:

1. polishing inside surface of an AlON dome to promote bonding of EMIgrid, unless the AlON dome has the desired surface smoothness, which isbelieved to be on the order of 10 μm RMS or better, on the innersurface;

2. applying an EMI grid to inside surface of the AlON dome;

3. bonding a BGG glass dome to interior surface of the AlON dome havingsecured thereto the EMI grid;

4. polishing the interior surface of the BGG glass and outer surface ofAlON dome to improve optical transmission; and

5. optionally applying anti-reflective (AR) coatings on the outersurface of AlON and/or the inner surface of the BGG glass in thecomposite dome.

The outer surface of the BGG glass dome need not be polished beforebonding to the AlON dome, due to the fact that the glass will flow whenheated above its softening temperature. However, to facilitate bonding,the outer surface of the BGG glass dome can be polished to the desiredsmoothness before bonding to the AlON dome.

In another embodiment, a germanate glass can be used as a glue tofacilitate bonding two AlON domes with or without an intermediate EMIgrid.

In yet another embodiment, a lower softening temperature glass can beused as a glue to, bond an AlON dome with a germanate glass dome with orwithout an intermediate EMI grid.

FIG. 1 is a schematic diagram of a composite dome 10 composed of AlONsubstrate 12 on the outside of the composite dome, bonded with an innerBGG glass 16 to the inner surface of the AlON substrate 12.Electromagnetic interference grid 20 is optionally disposed between AlON12 and BGG glass 16. The grid is typically made of gold intersectingwires of about 1.2 μm in diameter with spacings of about 0.1 mm. Theprecise position and thickness of the grid depends on the opticalrequirements. During fabrication of the composite, load and/or pressurecan be optionally used.

Another embodiment of forming AlON-BGG glass composite is shown in FIG.4, where glass acts as a glue to bond AlON panels together. Compositesof windows can be made by way of a half-lap joint. As shown in FIG. 4, apair of AlON substrates or panels 12 and 14 are joined at their edges 16and 18 by notching the edges to form exposed surfaces. At least one, andtypically all, exposed surfaces are coated with a thin layer of a BGGglass and the edges are joined and then bonded by heating the glass andthe AlON substrate edges to above the softening temperature of theglass. Following annealing and cooling to room temperature, a largecomposite is obtained by virtue of the strong bond between AlONsubstrates and the BGG glass. Matching coefficient of thermal expansionand refractive indices of the glass and AlON substrates can make thejoint nearly imperceptible.

The bond between the glass and the AlON substrates was tested by thermalcycling between −50° C. and +150° C. The joint was found to be stablewithout any sign of failure or delamination. The glass/AlON compositehas the rain and sand erosion resistance to withstand harshenvironmental conditions.

For certain applications, such as ceramic armor, where the AlONcomposite has been developed as a strong candidate material in faceshields, windshields, and the like, the glass coating/layer/substrate isutilized to keep polishing cost low. Glass possessing same or similarrefractive index as AlON, will not introduce any noticeable reflectionlosses and at the same time, will significantly reduce the polishingcosts by up to 50%. This is due to the principal fact that the glass canbe polished using traditional glass polishing techniques.

The invention is further described by the following examples.

EXAMPLE 1

This example demonstrates preparation of BGG glass of this invention.

Pursuant to this example, a 200 gram-batch of the approximatecomposition of 15 BaO-10 Ga₂O₃-5 Al₂O₃-70 GeO₂ was prepared by mixing46.74 grams of BaCO₃, 29.6 grams of Ga₂O₃, 8.05 grams of Al₂O₃ and115.61 grams of GeO₂. The glass batch was mixed for 30 minutes and thentransferred to a platinum crucible. The platinum crucible, containingthe batch material, was placed in a pre-melting furnace preheated to1350° C. The batch material was left in the furnace to melt for 10minutes and then quenched in air to make a cullet. The cullet was thentransferred to another crucible that was loaded into a sealed furnacewith a controlled atmosphere. The furnace was heated to 1300° C. underAr/O₂ atmosphere. The glass was bubbled with 80/20 mol ratio Ar/O₂mixture for 9 hours to remove water. After 9 hours of bubbling, thebubbling tube was pulled out of the melt, with the Ar/O₂ gasses stillflowing over the melt. The melt was left at 1300° C. for about another 3hours to fine and was then quenched in the sealed furnace and allowed tocool to below the glass transition temperature of 659° C. The cooledglass was then taken out of the crucible and annealed. Annealing wasperformed by placing the sample in an annealing oven at 690° C. for 2hours and then was slowly cooled to room temperature at 1° C. Bariumchloride, in amount of about 5% in the batch, can also be used to removeOH— ions to less than 1 ppm.

EXAMPLE 2

This example demonstrates joining a BGG glass substrate to an AlONsubstrate.

Glass of 12.5 BaO-2.5 BaCl₂ -10 Ga₂O₃ -5 Al₂O₃ -70 GeO₂ composition, wasobtained by the procedure described in Example 1, was cut into a1″-diameter disc of 1.5 mm thickness. The glass was polished on theinner surface, using a final 800 grit paper. The glass and the AlONsubstrates were cleaned using isopropyl alcohol and then placed indirect contact under a mild vacuum of less than 1 Torr and under a loadto obtain a pressure of about 100 psi during the bonding, i.e., heattreatment process. The samples were heated together from roomtemperature to 760° C. at a heating rate of 5° C. per minute. Thesamples were held at 760° C. for 1 hour and then cooled to 680° C. at acooling rate of 5° C. per minute. The samples were then held at 680° C.for 6 hours for annealing followed by slow cooling at a rate of 0.1° C.per minute down to room temperature. The product was a composite of theBGG and the AlON substrates shown in FIG. 3.

EXAMPLE 3

A polished AlON dome of dimensions 1.69 inches outside radius, 1.56inches inner radius with a dome thickness of 0.13 inches and dome heightof 1.54 inches was obtained. BGG glass dome was made by using a glassmelting process described in Example 1, above, and cast into dome shapeand annealed at 680° C. The glass dome was ground and polished to thedimensions of 1.56 inches outer diameter, 1.52 inches inner diameterwith a thickness of about 0.04 inches and dome height of 1.41 inches.The outer surface of the glass dome and inner surface of the AlON domewere cleaned in isopropyl alcohol. The BGG glass dome was fully placedinside the AlON dome to make full contact between outer surface of theBGG dome and the inner surface of the AlON dome. The domes were heatedtogether using heating cycle described in Example 2, above, to bond andanneal the BGG and the AlON domes. A BGG-AlON composite dome wasobtained with a very strong bond in between. The bonded dome wasrepeatedly cycled between −50° C. and +150° C. and after the test, thebonded composite dome indicated no sign of fracture or stresses orentrapped air.

EXAMPLE 4

This example is similar to Example 3, above, with the exception that anEMI grid was applied on the inside surface of the polished AlON domebefore bonding it with the BGG glass dome.

EXAMPLE 5

This example is similar to the one described in Example 3, above, withthe exception that during the entire bonding process, a vacuum of 1 Torrwas used.

EXAMPLE 6

This example is similar to Example 5. The bonded composite dome fromExample 5, above, was placed in a hot isostatic press (HIP) and heatedto 750° C. at 5° C./min. At 750° C., an isostatic pressure of 5,000 psiwas applied for 15 minutes while the sample was maintained at 750° C.After 15 minutes at 750° C., the isostatic pressure was released. Thesample was cooled at 5° C./minute to 680° C. and held for 3 hours forannealing. The sample was then cooled to room temperature at 0.1°C./minute. The bonded composite dome had no entrapped air pockets.

EXAMPLE 7

This example is similar to Example 6, above, with the exception that anEMI grid was on the inside surface of AlON dome before it was bonded tothe BGG glass dome, as used in Example 6.

While presently preferred embodiments have been shown of the novelcomposite and process for making it, and of the several modificationsdiscussed, persons skilled in this art will readily appreciate thevarious additional changes and modifications can be made withoutdeparting from the spirit of the invention as defined and differentiatedby the following claims.

1. A composite comprising Aluminum oxynitride, i.e., AlON, and agermanate glass bonded together having transmission in the mid-infraredwavelength region.
 2. The composite of claim 1 wherein said compositehas transmission in excess of 50% in the 0.4-5 μm wavelength region. 3.The composite of claim 2 wherein coefficient of thermal expansion ofAlON and said glass are within 1×10⁻⁶/K and wherein said composite hastransmission in excess of 60% in the 0.4-5 μm wavelength region.
 4. Thecomposite of claim 3 wherein said glass is a BGG glass that may containup to 10 mole % of other components selected from the group consistingof Al₂O₃, La₂O₃, ZnO, CaO, ZrO₂, In₂O₃, Y₂O₃, Gd₂O₃, Na₂O, K₂O, Cs₂O,Rb₂O, SrO and mixtures thereof.
 5. The composite of claim 4 wherein thecomposition of said glass, in mole percent, is 10-20 BaO/5-15 Ga₂O/3-10Al₂ 03/60-80 GeO₂.
 6. The composite of claim 1 which contains an EMIgrid.
 7. The composite of claim 4 wherein coefficient of thermalexpansion of said AlON and said glass are within 1×10⁻⁶/K and whereinsaid composite has transmission in excess of 60% in the 0.4-5 μmwavelength region.
 8. The composite of claim 7 wherein refractive indexof said AlON and said glass is within 0.1, wherein thickness of saidAlON is in the range of 1-5 mm and thickness of said glass is in therange of 0.1-5 mm, wherein said composite includes anti-reflectivecoating on the outer surface of said AlON and another anti-reflectivecoating on the inner surface of said germanate glass, and whereincrystallization temperature of said glass is above its glass transitiontemperature and its glass stability is in excess of 100° C.
 9. Acomposite comprising AlON articles bonded together with a germanateglass and having transmission in the mid-infrared wavelength region. 10.The composite of claim 9 wherein said glass is a BGG glass that caycontain up to 10% of other components selected from the group consistingof ZnO, SrO, CaO, ZrO₂, Y₂O₃, Gd₂O₃, Al₂O₃, La₂O₃, In₂O₃, Na₂O, K₂O,Rb₂O, Cs₂O, and mixtures thereof.
 11. A process of bonding an AlONarticle(s) and a germanate glass article(s) includes the step of heatingthem together above the softening temperature of the glass.
 12. Theprocess of claim 11 including the step of applying a vacuum during thebonding of the. AlON and the glass articles.
 13. The process of claim 12including the step of applying load during bonding of the AlON and theglass articles.
 14. The process of claim 13 including the step ofapplying a hot isostatic pressure to the bonded articles in order toeliminate any trapped air.
 15. The process of claim 13 whereincomposition of the glass, in mol percent, is 10-20 BaO/5-15 Ga₂O₃/3-10Al₂O₃/60-80 GeO₂.
 16. The process of claim 15 including the step ofpolishing inner surface of the glass article to about the same degreethat the AlON article would have been polished in the absence of theglass.
 17. A process of bonding at least two articles, at least one ofthe articles that is bonded is AlON, that includes the step of applyinga suitable germanate glass to at least one of the articles, joining thearticles together, heating the newly joined surfaces of the articles toabove the softening temperature of the glass, and bonding the articlesto each other.
 18. The process of claim 11 including the steps ofpolishing the inner surface of the AlON article, applying anelectromagnetic interference grid to the polished inner glass surface ofthe AlON article, bonding a germanate glass to the polished AlONarticles, and polishing inner surface of the glass and the outer surfaceof the AlON articles and wherein said bonding step includes the step ofheating the articles together above the glass softening temperature. 19.The process of claim 18 including the step of matching coefficient ofthermal expansion of the AlON and the germanate glass within 0.1×10⁻⁶/Kand refractive index thereof to within 0.05.
 20. The process of claim 19including the steps of removing OH⁻ from the glass to 1 ppm or below andapplying anti-reflective coating to the outside surface of the AlON andthe inside surface of the germanate glass articles.